Electrical conductivity of samarium-ytterbium zirconate ceramics
Electrochimica Acta 54(2009)3968-3971,-0001,():
(Sm1-xYbx)2Zr2O7 (0≤x≤1.0) ceramic powders were prepared by chemical-coprecipitation and calcinations method, and were pressureless-sintered at 1973K for 10h to fabricate dense bulk materials. (Sm1-xYbx)2Zr2O7 has a single phase with a pyrochlore or defect fluorite structure, depending mainly upon the Yb content. They are found to be pyrochlores for 0≤x≤0.1, and defect fluorites for 0.3≤x≤1.0. The electrical conductivity of (Sm1-xYbx)2Zr2O7 was investigated by complex impedance spectroscopy over a frequency range of 200Hz to 20MHz from723 to 1173K in air. The measured electrical conductivity obeys the Arrhenius relation. The grain conductivity of (Sm1-xYbx)2Zr2O7 ceramics gradually increases with increasing temperature. A decrease of about one order of magnitude in grain conductivity is found at all temperature levels when the Yb content increases from x=0.1 to x=0.3. The electrical conductivities of defect fluorite-type materials are lower than those of pyrochlore-type materials in (Sm1-xYbx)2Zr2O7 system, whereas activation energies for the conduction process increase monotonically as the structure becomes disordered
【免责声明】以下全部内容由[欧阳家虎]上传于[2009年04月30日 10时23分56秒],版权归原创者所有。本文仅代表作者本人观点,与本网站无关。本网站对文中陈述、观点判断保持中立,不对所包含内容的准确性、可靠性或完整性提供任何明示或暗示的保证。请读者仅作参考,并请自行承担全部责任。
本学者其他成果
同领域成果