Study on the structure and wear resistance of two-step salt bath nitrocarburized steel
Y.H. Qiang et al./Wear 218(1998)232-236,-0001,():
This paper deals with the investigation of two-step salt bath nitrocarburizing technologies. For comparison, ferritic nitrocarburizing was also conducted. By means of metallographic examination, microhardness test. X-ray diffraction analysis, the microstractere, phase construction, surface hardness and hardness profiles of case hardened layers on steel treated by various nitrocarburizing techniques were investigated. The friction coefficient and ring-on-block apparatuses were employed to investigate the friction coefficient and wear-resistance of case hardened layers. Meanwhile, the surface roughness of various nitrocarburized specimens was also tested by a stylus pmfilometer. The experimental results indicate that thicker compound layers are achieved on the specimen surfaces treated by two-step nitrocarburizing than by ferritic nitrocarbarizing; the phase constructions of two-step salt bath nitrecarburized specimen surfaces are different from that observed ou ferritic nitrocarburized specimens and two distinct layers are clearly visible on the cross-sections of two-step nitrocarburized specimens which consists predominately of E-compound (Fe3N) with a tiny minority of Fe3O4 (outer layer't and carbon/nitrogen martensite with a high percentage of austenite (inner later), while the phase construction of specimen surfaces treated by ferritic nitrocarburizing is composed mainly of e-compound (Fe; N) and a small amount of Fe4N and Fe2-3N.
【免责声明】以下全部内容由[强颖怀]上传于[2009年02月10日 14时09分44秒],版权归原创者所有。本文仅代表作者本人观点,与本网站无关。本网站对文中陈述、观点判断保持中立,不对所包含内容的准确性、可靠性或完整性提供任何明示或暗示的保证。请读者仅作参考,并请自行承担全部责任。
本学者其他成果
同领域成果