牙用烤瓷支架钴铬钼合金的支架及冠适合性的研究

首发时间：2005-12-22

刘长虹 ¹ 杨晓喻 ¹ 巢永烈 ² 李宁 ³

1、广东省口腔医院
2、四川大学华西口腔医学院修复科
3、四川大学金属材料学院

摘要：[摘要] 目的: 研究DA9-4合金支架及冠适合性，为该合金的临床应用奠定基础。方法: ①支架适合性的测试：制作上颌651∣156 缺失标准模20个，常规制作蜡型。随机分成两组，每组10个，分别用DA9-4合金、Reminium 2000合金铸造。用测量显微镜测量蜡型及铸造支架的距离差，计算铸造收缩量。②冠适合性测试：制作有机玻璃模具30件。硅橡胶印模材料翻制成超硬石膏模型。常规制作帽状冠的蜡型。试件随机分成三组，每组10件，用DA9-4合金、Reminium 2000合金及VB钢铸造。粘结后的样本沿模具底座中部纵向剖开。体视显微镜测量试件10个部位粘结剂的厚度。结果: DA9-4合金与Reminium 2000合金铸造支架收缩无显著性差异（P>0.05）。DA9-4合金冠修复体边缘间隙为71.3±8.34μm、肩台间隙为53.4±4.83μm、轴面间隙为41.85±8.08μm、

关键词：适合性钴铬钼合金冠修复铸造支架

For information in English, please click here

The study of the crown and framework fitness of Co-Cr-Mo alloys

Liu Changhong ¹ Yang xiaoyu ¹ Chao Yonglie ² Li Ning ³

1、Guangdong Provincial Stomatological hospital
2、Department 0f Prosthodontics West China College of Stomatology - Si Chuan University
3、College of metallic material- Si Chuan University

Abstract：Objective: To investigate the crown and framework fitness of the Co-Cr-Mo alloy, and for clinic use. Methods: ①20 maxillary dentue mould which lose 651∣156, The speciments were grouped equally into ten. Waved and casted with DA9-4 alloys and Reminium 2000 alloys, respectively. Measure the distance of wax and the framework with microscope. And then calculate the amount of shrink after cast. ②Thirty crown speciments, the shape as per-molar after preparation. The speciments were grouped equally into ten. Cast with DA9-4 alloys; Reminium 2000 alloys and VB alloys, respectively. Each speciment was sandblasted with alumina and bonded with Hy-Bond Glassionomer. After bond, the speciments were embed with self- coagulated plastic and cut longitudinal at the middle. Measure 10 spots of the thick between the crown and the speciments with stereomicroscope. Results: The cast shrink between DA9-4 alloys and Reminium 2000 alloys are no significant difference(P>0.05). And the fitness of the crown are: the margin gap of the crown is 71.3±8.34μm, the shoulder gap is 53.4±4.83μm, the axial wall gap is 1.85±8.08μm, the occlusal lift amount is 55.2±9.21μm. Conclusion: The result showed that the alloy has good fitness and can meet the require of clinic.

Keywords： fitness Co-Cr-Mo alloys framework Crown restoration

基金：

1. 教育部博士点基金（20020610066）

论文图表：

引用

导出参考文献

.txt

.ris

.doc

刘长虹，杨晓喻，巢永烈，等. 牙用烤瓷支架钴铬钼合金的支架及冠适合性的研究[EB/OL]. 北京：中国科技论文在线 [2005-12-22]. https://www.paper.edu.cn/releasepaper/content/200512-556.

No.4555379691135216****

同行评议

共计0人参与

全部评论

0/1000

论文编号	200512-556
论文题目	牙用烤瓷支架钴铬钼合金的支架及冠适合性的研究
文献类型
收录期刊	上传封面中文期刊英文期刊期刊名称（中文）期刊名称（英文）年，卷（）上传封面中文专著英文专著书名（中文）书名（英文）出版地出版社出版年上传封面中文译著英文译著书名（中文）书名（英文）出版地出版社出版年上传封面中文论文集英文论文集编者.论文集名称（中文） [c]. 出版地出版社出版年， - 编者.论文集名称（英文） [c]. 出版地出版社出版年，- 上传封面中文文献英文文献期刊名称（中文）期刊名称（英文）日期-- 在线地址http:// 上传封面中文文献英文文献文题（中文）文题（英文）出版地出版社,出版日期-- 上传封面中文文献英文文献文题（中文）文题（英文）出版地出版社,出版日期--
英文作者写法：中外文作者均姓前名后，姓大写，名的第一个字母大写，姓全称写出，名可只写第一个字母，其后不加实心圆点“.”, 作者之间用逗号“，”分隔，最后为实心圆点“.”, 示例1：原姓名写法：Albert Einstein,编入参考文献时写法：Einstein A. 示例2：原姓名写法：李时珍；编入参考文献时写法：LI S Z. 示例3：YELLAND R L,JONES S C,EASTON K S,et al.