残余元素铜在中碳钢中的析出规律
首发时间:2008-11-20
摘要:以中碳钢为研究对象,调整Mn、S含量,添加0.3%左右的铜作为残余元素,研究铜在钢中的偏析以及在夹杂物上的析出情况。利用扫描电镜及能谱仪研究发现当钢中锰含量从0.008%提高到0.094%时,可以减轻铜沿原奥氏体晶界的偏析程度。锰含量为0.440%时,铜在硫化锰夹杂上的析出比例可以达到94.6%,继续提高锰含量对提高铜的析出比例无益。通过二元匹配度的计算,可以得出,无论Cu在钢中以何种形式存在,MnS夹杂较氧化硅、氧化铝夹杂更适合铜析出,计算结果与实验结果吻合。
For information in English, please click here
Copper precipitation behavior in medium carbon steel
Abstract:In this study, about 0.30% copper is added into medium carbon steel as residual element, The content of manganese and sulfur is varied to investigate on their effect on copper precipitation in inclusion,and copper intergranular segregation on the grain boundary during cooling. When the manganese content is changed from 0.008% to 0.094%, the segregation of copper on the grain boundary is less. When the manganese content is 0.440%, the proportion of copper precipitation in manganese sulfide to the total sulfide is 94.6%. Further increase of the manganese content is not helpful for increasing the proportion of copper precipitation. The disregistry between the lattice parameters of the copper particles and the inclusions is calculated, which proves manganese sulfide is more favorable for copper precipitation than silicon oxide and aluminum oxide as inclusions.
Keywords: segregation copper precipitation disregistry medium carbon steel copper manganese sulfide inclusion
论文图表:
引用
No.2589422269122714****
同行评议
勘误表
残余元素铜在中碳钢中的析出规律
评论
全部评论0/1000