Formation and Thermal Fatigue Properties of Fine-grained Heat Affected Zone on Cast-hot-working-die Steel after Electropulsing Stimulation with High Current Density
首发时间:2008-12-31
Abstract:The fatigue crack propagation behaviors of cast-hot-working die (CHWD) steel untreated and treated by electropulsing stimulation with different current densities were investigated in the present study. The elliptical heat affected zone (HAZ) was formed ahead of specimen notch tip due to the concentrating heat release induced by current bypassing and concentrating effect. The acreages of specimen HAZs were gradually enlarged because of the more heat energy input by elevating current density of electropulsing stimulation. The grain refinement and dislocation density increase in the specimen HAZs were enhanced by elevating the current density of electropulsing stimulation, which inevitably resulted in the improvement on the HAZ mechanical properties and the enhance of fatigue resistance. In addition, the induced compressive stress by electropulsing stimulation could decrease the peak value of tensile stress forming in the thermal fatigue process, which also enhanced the thermal fatigue resistance. Consequently, the resistance to thermal fatigue of CHWD steel was enhanced by grain refinement, dislocation density increase and induced compressive stress after electropulsing stimulation with high current density.
keywords: thermal fatigue electropulsing stimulation CHWD steel
点击查看论文中文信息
论文图表:
引用
No.2718037361612307****
同行评议
共计0人参与
勘误表
高密度脉冲电流作用下细晶粒热影响区的形成和热疲劳性能
评论
全部评论0/1000