Effect of boron underlayer on ordering and orientation of sputtered FePt film
首发时间:2011-02-18
Abstract:FePt multilayer films with a boron underlayer were prepared on Si (100) substrates using magnetron sputtering, and a subsequent vacuum annealing was carried out to obtain the hard magnetic L10 phase. According to the XRD results, the ordering of the FePt films is facilitated at low annealing temperatures while is blocked at high ones by introducing the boron. Moreover, (001) orientation of the samples is obviously improved by inserting a born underlayer, which is further confirmed by the MFM analysis. The relevant mechanism is discussed by considering the diffusion of boron atoms and a consequential in-plane tensile stress.
keywords: Magnetron sputtering Crystal structure Boron underlayer L10 FePt film Magnetic recording materials
点击查看论文中文信息
硼底层对溅射制备FePt薄膜有序化和取向的作用
摘要:在室温的单晶Si基片上利用磁控溅射制备了带有B底层的FePt多层薄膜,通过真空退火得到了具有硬磁性的L10相。结构和磁性分析表明,B底层在400 oC以下有利于FePt的相变,而在更高温度下则会抑制金属原子的相互扩散。此外,应当与B原子渗入合金晶格导致的面内张应力有关,底层的添加促进了FePt晶粒的垂直取向,获得了更好的(001)织构,有利于薄膜应用为垂直磁记录材料。
关键词: 磁控溅射 晶格结构 硼底层 L10相FePt薄膜 磁记录材料
论文图表:
引用
No.4409676555276129****
同行评议
共计0人参与
勘误表
硼底层对溅射制备FePt薄膜有序化和取向的作用
评论
全部评论0/1000