摘要:采用双氰胺为功能单体、以甲醛为交联剂,对制革废弃牛毛提取的角蛋白进行改性,用红外光谱、粒径分析等进行了表征,并进一步制备制革专用角蛋白填料,回用于制革填充工序。研究表明,当角蛋白与双氰胺质量比为1:0.5,双氰胺与甲醛的物质的量比为1:3,羟甲基化时间为1h,共聚时间为0.5h时,改性蛋白填料填充皮革的增厚率最高;将蛋白填料应用到制革中,蛋白填料用量为10%,所得皮革增厚率为41.8%,粒面平细,手感柔软丰满,物理机械性能好。
For information in English, please click here
Study on Preparation of Protein Filler by Dicyandiamide Modified Keratin
Abstract:Dicyandiamide was used as functional monomer and formaldehyde was used as crosslinking agent to modify the keratin extracted from cow hair in leather-making industry, the IR spectra, particle size analysis and so on were used to characterize. And further preparation of leather special protein fillers, used for tanning filling process. Research shows that: When the mass ratio of keratin to dicyandiamide was 1: 0.5, The molar ratio of dicyandiamide to formaldehyde is 1: 3, The methylation time was 1 h, The copolymerization time was 0.5 h, the thickening rate of the modified protein filler is the highest. The protein filler was applied to the leather,when the amount of protein filler 10%, the resulting leather thickening rate of 41.8%, the grain was fine,the sensory proStudy on Preparation of Protein Filler for Tannery by Dicyandiamide Modified Keratinperties were soft and plump, physical and mechanical properties were fine.
Keywords: kkeratin Dicyandiamide modification protein filling
论文图表:
引用
No.4734283617497149****
同行评议
共计0人参与
勘误表
双氰胺改性角蛋白填料的制备与应用
评论
全部评论0/1000