Raman Analysis of a Crystalline SiC Sample Prepared from Carbon-Saturated Melt of Silicon
CHIN. PHYS. LETT. Vol. 18, No. 8 (2001) 1123,-0001,():
Crystalline SiC samples were prepared in solidification of silicon melt saturated by carbon solved from the inner wall of a graphite crucible. The crystalline structure of the samples was analysed in Raman spectroscopy and confirmed as 3C-SiC both in x-ray diffraction and x-ray photoelectron spectroscopy (XPS). The Raman spectra of the samples present a strong sharp peak located at 796.3cm-1 with a full width at half maximum about 6cm-1 and three weak peaks broadened around 1525.6, 1631.4 and 1719.1cm-1, respectively. The former belongs to the transverse optical phonons of 3C-SiC, while the latter can be attributed to the second-order scattering. However, the longitudinal optical mode of 3C SiC has not been found for our samples. An additional broadened peak at 532.2 cm-1 may imply the existence of some lattice defect in the samples, which is related to nitrogen introduced unintentionally into the lattice in the growth process and confirmed in XPS of N 1s binding energy centred at 400.9 eV.
【免责声明】以下全部内容由[陈治明]上传于[2007年05月31日 11时56分32秒],版权归原创者所有。本文仅代表作者本人观点,与本网站无关。本网站对文中陈述、观点判断保持中立,不对所包含内容的准确性、可靠性或完整性提供任何明示或暗示的保证。请读者仅作参考,并请自行承担全部责任。
本学者其他成果
同领域成果