Simple fabrication of twist-like helix N,S-codoped titaniaphotocatalyst with visible-light response
Applied Catalysis B: Environmental 79(2008)72-80,-0001,():
Visible-light responsible N,S-codoped titania photocatalyst was fabricated by simple hydrolysis of titania tetrachloride using ammonia in the presence of glacial acetic acid and ammonium sulfate. The N,S-codoped titania materials were fabricated by a template-free route and demonstrated twist-like helix morphology. The morphology and microstructure characteristics of N,S-codoped titania photocatalysts were characterized by means of the N2 adsorption-desorption measurements, thermal gravimetric and differential thermal analysis (TG-DTA), transmission electron microscopy (TEM), scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), Fourier transform infrared spectroscopy (FT-IR), UV-visible diffuse reflectance spectra (DRS) and X-ray powder diffraction (XRD). The unique morphology of N,Scodoped titania materials and mesoporous microstructure were maintained after a heat treatment at 723 K for 3 h, exhibiting significantly thermal stability. The photocatalytic activity was evaluated by degrading phenol in aqueous suspension under ultraviolet and visible light irradiation. The results obtained with these novel photocatalysts are compared with the behavior of the well-studied and widely used Degussa P25 TiO2 under the same conditions. The N,S-codoped titania samples were more superior than P25 and the sample calcined under 723 K for 3 h shows the best photocatalytic activity, the higher activity of which could be attributed to its high surface area, large pore volume, well-crystallized anatase, redshift in adsorption edge and strong absorbance of light with longer wavelength.
【免责声明】以下全部内容由[戴维林]上传于[2010年12月13日 14时57分14秒],版权归原创者所有。本文仅代表作者本人观点,与本网站无关。本网站对文中陈述、观点判断保持中立,不对所包含内容的准确性、可靠性或完整性提供任何明示或暗示的保证。请读者仅作参考,并请自行承担全部责任。
本学者其他成果
同领域成果