BULK ALUMINA SUPPORT WITH HIGH TOLERANT STRAIN AND ITS REINFORCING MECHANISMS
Acta mater 49(2001)1939-1946,-0001,():
Bulk porous Al2O3 support was fabricated using a mixture of fine α-Al2O3 powder and Al(OH)3 particles, followed by pressureless sintering at temperatures between 1100°C and 1300°C. Al2O3 support with high surface area was obtained, due to the presence of transitional Al2O3 phases that were produced by the decomposition of Al(OH)3 even after sintering. The Al2O3 support exhibited superior mechanical properties and high strain to failure, compared with those fabricated by traditional methods. The strain to failure increased with the amount of Al(OH)3 in the mixture, but decreased with increasing sintering temperature. A conceptual model for the microstructural evolution and reinforcing mechanisms, based on transmission electron microscopy (TEM) observations, is proposed. It reveals that the interface bonding of the Al2O3 boundaries formed at the initial nucleation stage during θ- to α-Al2O3 transformation is stronger than that formed by subsequent grain growth. The interface bonding between the Al2O3 grains, which came from the decomposition of Al(OH)3, is stronger than that between the original Al2O3 grains in the starting mixture. 2001 Acta Materialia Inc. Published by Elsevier Science Ltd. All rights reserved.
【免责声明】以下全部内容由[邓振炎]上传于[2011年05月18日 10时08分57秒],版权归原创者所有。本文仅代表作者本人观点,与本网站无关。本网站对文中陈述、观点判断保持中立,不对所包含内容的准确性、可靠性或完整性提供任何明示或暗示的保证。请读者仅作参考,并请自行承担全部责任。
本学者其他成果
同领域成果