Introduction of the ultrafine MgO to the high Tc melt-texture YBa2 Cu3 O7-δ*
Physica C 282-287 (1997) 547-548，-0001，（）：
idth at half-height of powder X-ray diffraction, the MgO powder was about 20nm in size on average. A supersonic vibration was introduced to destroy the accumulation of the ultrafme powder and to mix the powder with the YBa2 Cu3 07-δ precursor. The melt-process was employed to grow textured samples. From the Scanning Electron Microscope (SEM) graphs, some particles were found in the textured samples, which were about several nanometer in size. The composition of these particles, however, leaves to be identified. The magnetic critical current density (Jcm) at 77K dropped rapidly with the increase of Mg content.