Sol-gel synthesis and photoluminescence of AlP nanocrystals embedded in silica glasses
H. Yang et al./Optical Materials 29(2007)747-752,-0001,():
A1P nanocrystals embedded in silica glasses were prepared via an easy sol-gel process. The gels synthesized by the hydrolysis of a complex solution of Si (OC2H5) 4, A1 (NO3)3 Æ9H2O and PO (OC2H5) 3 were heated at 600℃ for 10h in an air atmosphere to form an Al2O3-P2O5-SiO2 gel glass. The gel glasses were then heated in the presence of H2-N2 mixed gas, in which the P(V) are reduced by the H2 gas, and react with Al (Ⅲ) to form fine cubic A1P crystallites embedded in silica glasses. The X-ray diffraction patterns showed (111), (220), and (311) diffraction lines from cubic AlP crystals. The AlP (220), (311), (422), and (440) diffraction lines were observed in the electron diffraction pattern. The size of AlP nanocrystals was found to be from 5 to 10nm in diameter by transmission electron microscopy. A strong room temperature photoluminescence (PL) with peaks at 533, 582, 649, and 688nm was observed from AlP/SiO2 nanocomposites. The PL is suggested to originate from the hydrogen-related species (PL band at 533nm), the small "peroxy radical" (PL band at 582nm), and the nonbridging oxygens (PL bands at 649 and 688nm), respectively.
【免责声明】以下全部内容由[黄大鸣]上传于[2009年02月17日 15时30分30秒],版权归原创者所有。本文仅代表作者本人观点,与本网站无关。本网站对文中陈述、观点判断保持中立,不对所包含内容的准确性、可靠性或完整性提供任何明示或暗示的保证。请读者仅作参考,并请自行承担全部责任。
本学者其他成果
同领域成果