Understandings on the scattering property of the mechanical strength data of solid catalysts A statistical analysis of iron-based high-temperature water-gas shift catalysts
Catalysis Today 51(1999)73-84,-0001,():
Statistics reveal that horizontal crushing strength data scatter in rather large ranges for cylindrical iron-based hightemperature water-gas shift catalyst tablets. This scattering is due to brittle fracture nature of the strength failure, originating from the stress concentration around edges of existing micro-cracks, such as pores, defects, and discontinuations contained in tablets. However, variations in the tablet size and density are found to contribute to strength data scattering. Data of tablet strength, height and density of the catalysts are found to be scattered in different ranges and to follow Weibull distribution, respectively. Based on the statistical data from a number of commercial catalysts, strength failure probability is proposed as the critical parameter for quality control. Catalyst tablet texture is examined, and it is observed that the tablets with strength close to low end of strength distribution have higher porosity, lower density and larger pore size in comparison with those near high end. For catalyst tablets, low strength is related to increased risk of strength failure, and high strength would result in lower catalyst ef
【免责声明】以下全部内容由[李永丹]上传于[2005年01月18日 21时19分25秒],版权归原创者所有。本文仅代表作者本人观点,与本网站无关。本网站对文中陈述、观点判断保持中立,不对所包含内容的准确性、可靠性或完整性提供任何明示或暗示的保证。请读者仅作参考,并请自行承担全部责任。
本学者其他成果
同领域成果