Mo-Si-Al-C-based multiphase compounds and their composites reinforced by micro-SiC and TiC particulates were manufactured by meansof reactive hot-pressed sintering method. Their microstructure and room temperature mechanical properties were studied. The results showedthat Al addition and the ratio of Si/Al exerted a remarkable effect on the reaction products in the Mo-Si-Al-C systems. For the stoichiometricMo5(Si,Al)3C mixed powders with a molar ratio of Mo∶Si∶Al∶C as 5∶1.5∶1.5∶1, the sintered body contained Mo3Si, Mo3Al2C, and Mo5Si3C as themajor reaction products whereas and the minor phases consisted of MoSi2, Mo2C, and Mo(Si,Al)2 compounds. When the starting powder mixturewas off-stoichiometric with a small amount of excess Si, only Mo2C accounted for the minor product. Moreover, the relative contents of the formerthree major phases were affected by the changed Si/Al ratio, where the amounts of Mo3Al2C and Mo5Si3C compounds decreased and increased,respectively with increasing Si/Al ratio. The two multiphase alloys showed poor mechanical properties, due to the existence of residual porosity.In contrast, the composites exhibited superiority in both flexural strength and fracture toughness at room temperature to the Mo-Si-Al-C-basedmultiphase compounds. MSAC1/20 wt.%SiC and MSAC1/20 wt.%TiC composites had a respective flexural strength and fracture toughness of 454and 438MPa, 4.93 and 4.85MPa√m.