Comparative Study of Corrosion-Fatigue in Aircraft Materials
AIAA JOURNAL Vol. 39, No.2, February 2001,-0001,():
Corrosion-fatigue is one of the damage mechanisms affecting the structural integrity of the aging aircraft. Simple analytical and probabilistic models for predicting pitting corrosion and corrosion-fatigue life in aluminum alloy 2024/T3 used in aircraft structures is presented. The developedmodel includes the effect of the interaction of cyclic load and the corrosive environment on the fatigue life, and considers all stages of the corrosion-fatigue process. The probabilistic model investigated considers the uncertainties in initial pit size, corrosion pitting current, and material properties due to scatter found in the experimental data.The analytical model shows very good quantitative agreement with the existing experimental data and analytical models over a wide range of parameters. The results predicted that the crack initiation life varies approximately 10-40% as compared to crack propagation life in corrosion-fatigue problems.
【免责声明】以下全部内容由[王清远]上传于[2005年07月28日 17时40分12秒],版权归原创者所有。本文仅代表作者本人观点,与本网站无关。本网站对文中陈述、观点判断保持中立,不对所包含内容的准确性、可靠性或完整性提供任何明示或暗示的保证。请读者仅作参考,并请自行承担全部责任。
本学者其他成果
同领域成果