The fretting behavior of superelastic nickel titanium (NiTi) shape memory alloy was studied at various displacement amplitudes on a serve-hydraulic dynamic test machine. The results showed that the superelastic properties of the material played a key role in the observed excellent fretting behavior of NiTi alloy. Due to the low phase transition stress (only 1/4 the value of its plastic ield stress) and the large recoverable phase transition strain (5%) of NiTi, the friction force of NiTi/GCr15 stainless steel pair is smaller than the value of GCr15/GCr15 pair and at the same time the Rabinowicz wear coefficient of NiTi plate is about 1/9 the value of GCr15 plate under the same fretting conditions. For NiTi/GCr15 pair, even NiTi has a much lower hardness than GCr15, the superelastic NiTi alloy exhibits superior fretting wear property than GCr15 steel. It was found that the weak ploughing was the main wear mechanism of NiTi alloy in the partial slip regime. While in the mixed regime and gross slip regime, the wear of NiTi was mainly caused by the abrasive wear of the GCr15 debris in the three-body wear mode.

Using friction force microscopy (FFM) under controlled environments, we have systematically investigated the humidity effect on the frictional properties of two important classes of self-assembled monolayers (SAMs), i.e., N-octadecyltrimethoxysilane (OTE,CH3(CH2)17Si(OCH3)3) on SiO2 (OTE/SiO2); and N-alkanethiols on Au (111), together with their respective substrates. Experimental results show that both OTE and alkylthiol SAMs can decrease the friction force between a Si3N4 atomic force microscope (AFM) tip and substrates. The nearly humidity-independent friction of the two kinds of SAMs indicates that these SAMs are ideal lubricants in applications of micro-electro-mechanical systems (MEMS) under different environments. The humidity dependence-as the humidity increases, the friction first increases and then decreases-of the two substrates, SiO2 and Au (111), can be explained by the adsorption of water. The decrease in the friction at high humidity is attributed to the low viscosity in the multilayers of water, while the increase in the friction at low humidity can be explained by the high viscosity between the water monolayer and the surfaces (AFM tip and sample), possibly due to the confinement effects. The effect of modification of the AFM tip with alkanethiol molecules on the humidity dependence of Au (111) friction has also been investigated.

采用光干涉法相对光强原理对点接触中心区进行了润滑膜厚度测量，该方法在垂直方向的分辨率可达O.5nm，水平方向可达1μm，讨论了膜厚与压力，速度和润滑油粘度之刘的关系，观察和分析了流体润滑膜的失效现象。实验结果表明如果接触压力足够小或者润滑油粘度足够高，即使在一个很低的速度下也能清晰地观察到流体动压润滑效应。当压力增至某一定值，在膜厚-速度曲线上可观察到一个转辑点，当速度降到此点以下时，润滑膜厚度将很快减小到几个分子层厚，此时，润滑膜不再具有流体润滑特征，即流体润滑膜失效，失效点会出现在不同的速度和压力下。要使接触区在较高的压力下形成流体膜就必须加更高的速度或使用更大粘魔的润滑油。最后建立了失效点的压力、速度和润滑油粘度之间的关系。

We have studied the behavior of microwear and hardness of a superelastic nickel-titanium alloy using a triboindenter at various temperatures. Wear resistance was found to anomalously decrease with an increase in hardness. The observations are analyzed based on simple contact theory which suggests that the increase of hardness with the temperature is mainly due to an increase in phase transition stress, while the decrease of wear resistance with the temperature is due to an increase of the austenite elastic modulus and a decrease of the amount of phase transition that can be recovered.

For the friction measurements with AFM/FFM, usually the relative values of friction signal can be obtained. In order to compare the micro-tribological properties of different samples, mica is often used as an reference sample for friction measurement. However, due to the friction force of new cleaved mica surface is unstable, it is urged to systematically investigate the tribological properties of mica to design the experimental rules of the reference sample mica for friction measurements. Experimental results show that the friction of mica varies with the cleaving time, humidity and surface state of tip. The friction measured with different tips on mica varies in the range of