Using YBCO/MgO thin films, for the first time, we report a success in the melt-textured growth of YBCO bulks by the cold-seeding method. The grown bulk has a good orientation relation of YBCO 〈100〉 bulk Ⅱ YBCO 〈100〉 film Ⅱ MgO 〈100〉 substrate. In this process, the YBCO film withstood heating over its peritectic temperature (up to 1045℃) for 1.5 h and acted as a seed for the YBCO bulk growth, indicating an intrinsic superheating property, which was reported in other work. The unique superheating mechanism in this study was clarified. It was found that the a-b alignment of YBCO film plays a key role in controlling the single grain growth of YBCO bulk.

The effects of oxygen partial pressure on Y123 single-crystal growth, morphology and properties were inves-tigated. YBCO (Y123) single crystals were fabricated using the crystal pulling method under 1 atm partial pressure played a significant role in increasing growth rate, which was 1.5-2.5 times higher than that of crystals fabricated under air atmosphere. A large crystal with size of 19.8

In the air atmosphere, high superconducting transition temperature (Tc) Nd1+χBa2-χCu3O7-δ (NdBCO) single crystals were grown by top-seeded solution-growth (TSSG) Two controllable thermodynamical parameters, i.e. liquid composition and growth temperature were focused on. Using the ratio of Ba to Cu (Ba:Cu) at 0.78 in the liquid, the grown NdBCO crystal displays onset Tc of 94.6K with a sharp transition width DT less than 1.5K. The Ba-rich liquid leads to the lower substitution of Ba with Nd in grown crystals, resulting in the higher Tc. This finding suggests that the Ba: Cu ratio in the liquid is a very important processing parameter for obtaining higher Tc of the NdBCO uperconductors. In addition, the higher Tc as well as the lower Nd substitution can be achieved when using the lower growth temperature. These results are consistently interpreted by the NdO1.5-BaO-CuO ternary phase diagram.

The growth of REBa2Cu3O7-δ (REBCOZrare earth elements) high-temperature superconducting thick films by liquid phase epitaxy is reviewed, which are most promising for electronic device and coated conductor applications. The paper focused on thermodynamic relations, chemical reactions and physical phenomena in the liquid phase epitaxy process, which are closely related to the control of the microstructures and properties of materials. Recent progresses achieved and the problems to be solved have been reviewed in above sections.

A low solubility of yttrium in the Ba-Cu-O melt and a steep liquidus slope near the peritectic temperature Tp lead to a very slow growth rate of YBa2Cu3O7-δ(YBCO or Y123) single crystals and this creates a problem in growth of large single crystals. To solve this problem, increasing the growth rate and extending the growth time are significant. Using the crystal pulling method, we have developed several processes and succeeded in growing large Y123 and Nd1−χBa2+χCu3O7−(NδBCO) single crystals with an edge size over 25mm in the a-b plane and up to 20mm in the c-axis direction. In this article, three methods of increasing growth rate are reviewed. They are (i) employing high oxygen partial pressure, (ii) choosing RE (rare earth) elements with higher solubilities in the Ba-Cu-O solution, and (iii) growing REBCO crystals including several RE elements. Using these methods the growth rate was effectively enhanced from two to five times that of Y123. The critical temperature Tc of 92.7 K was achieved from a Y123 single crystal grown under 1 atm oxygen partial pressure, indicating that Tc is insensitive to the oxygen pressure of the growth atmosphere in the YBCO system. A high Tc of about 95 K for NdBCO superconductors with a sharp transition was obtained by controlling the ratio of Ba to Cu (Ba/Cu) in the liquid, suggesting that the Ba/Cu ratio in the liquid composition has a significant importance in controlling Tc. By partial substitution of Sm at the Y sites up to 30%, Y1−xSmx Ba2Cu3O7−(Y(Sm)BCO) crystals show a Tc of 91±1K and do not display Tc depression.