The corrosion resistance of Ni200, EB26 1, SHOMAC, MON EL400, 15 5PH, 3RE60, 304L and 316L alloys in chlorine and al kali industrial environment is determined by weight loss measure ments, microscopy and energy dispersive spectrometer. It is shown that welding does not deteriorate the corrosion resistance of the al loys except SHOMAC. Pitting corrosion and intergranular corrosion are present and the corrosion rates are a function of tempera ture and existence of CI and absorption of tramp elements on grain boundaries. According to the experiments, optimal selection of alloys for elevators working at different temperatures is suggested. Der Korrosionswiderstand yon Ni200, EB26 1, SHOMAC, MO NEL400, 15 5PH, 3RE60, 304L trod 316L Legierungen in indu strieller Chlor und Alkaliarngebung wurde mittels Gewichtsver lustmessungen, Gefftgeaufnahmen sowie energiedispersivem Spek trometer bestimmt. Es konnte gezeigt werden, dass das Schweigen den Korrosionswiderstand der Legiernngen, mit Ausnahme der Legiernng SHOMAC, nicht verschlechtert. Lochkorrosion trod inter kristalline Korrosion treten atff und die Korrosionsgeschwindigkei ten sind eine Ftmktion der Temperatur, der Anwesenheit yon Chlo ridionen und der Absorption yon Begleitelementen auf den Korn grenzen. Entsprechend den Ergebnissen der Versuche wird eine op timale Auswahl der Legiertmgen ffLr die bei verchiedenen Tempe rataren arbeitenden FOrdereinrichtungen vorgeschlagen.