Boundary liquation and interface cracking characterization in laser deposition of Inconel 738 on directionally solidified Ni-based superalloy，成果详细信息-中国科技论文在线

钟敏霖

146浏览
0点赞
0收藏
0分享
657下载
0评论
引用

期刊论文

Boundary liquation and interface cracking characterization in laser deposition of Inconel 738 on directionally solidified Ni-based superalloy

钟敏霖， Minlin Zhong* ， Hongqing Sun ， Wenjin Liu ， Xiaofeng Zhu ， Jinjiang He

Scripta Materialia 53 (2005) 159-164，-0001，（）：

URL:

摘要/描述

Laser deposition of Inconel 738 on directionally solidified (DS) Ni-based superalloy demonstrates a strong susceptibility to cracking. Cracks originate from the liquation of low melting point eutectic on the DS grain boundary. Five boundary liquation and interface cracking styles were identified. Sound Inconel 738 deposition layers were achieved free of cracks.

关键词: Nickel alloys ， Laser deposition ， Liquation cracking ， Superalloys ， Directional solidification