Polyvinyl chloride (PVC)/organic-montmorillonite composites were prepared by melt intercalation. Their structures and properties were investigated with X-ray diffraction (XRD), differential scanning calorimetry (DSC) and mechanical testing. The results showed that PVC chains could be intercalated into the gallery of organically modified montmorillonite to form exfoliated PVC/organic-montmorillonite nanocomposites, and the glass transition temperatures of PVC/organic-montmorillonite composites were lower than that of neat PVC. However, the tensile strength, and both the Izod type and Charpy notched impact strengths of PVC/organic-montmorillonite nanocomposites were fitted with the linear expressions: τ=535.07-6.39Tg, σI=378.76-4.59Tg and σC=276.29-3.59Tg, respectively

at lower temperature (<90℃) and decreases to 2 as the temperature increases. The addition of Org-MMT has no obvious effect on the apparent activation energy of the cure reaction. There is no special curing process required for the formation of an epoxy resin/Org-MMT/imidazole intercalated nanocomposite.