【期刊论文】Relationship between columnar crystal spacing and electric current density in unidirectional solidif ication of monophase Cu-Al alloy①

吴春京， CHANG Guo-wei， CAO Li-yun， YUAN Jun-ping， WAN G Zi-dong， WU Chun-jing， HU Han-qi

Trans. Nonferrous Met. Soc. China Vol. 12 No.5 Oct. 2002，-0001，（）：

-1年11月30日

摘要

On the basis of previous theoretical inferential relationship between the columnar crystal spacing and the density of electric current applied during unidirectional solidification, the effect of current density on the columnar crystal spacing was discussed and analyzed, and the experiment was made to verify the theoretical relationship. The results show that at fast solidification speed the columnar crystal spacing decreases with increasing the density of electric current, while at slow solidification speed the columnar crystal spacing increases with increasing the density of electric current. The critical conditions for the evolution of columnar crystal spacing were confirmed. The calculated values concerning the spacingand the density are consistent with the experimental results.

unidirectional solidification， columnar crystal spacing， effect of electric current， Cu-Al alloy

38浏览
0点赞
0收藏
0分享
68下载
0

引用

上传时间

2005年06月17日

【期刊论文】双结晶器连铸铜-锌铝合金双金属复合材料*

吴春京，吴春京***，谢建新，赵立华，王自东，周成

，-0001，（）：

-1年11月30日

摘要

设计和制造了1台双金属双结晶器连续铸造试验机，其特征是：①结晶器为水冷铜套内衬石墨套；②结晶器上面连接可控制温度的熔化保温炉；③在高度方向上设置一高一低、直径一小一大的结晶器。在此试验机上，成功地连续铸造出芯部直径<20mm的铜合金，外层厚度为10mm的锌铝合金的双金属复合圆棒。通过测试和分析此复合圆棒的宏观和微观的复合断面、化学成分分布、复合界面的剪切强度，证明此连续铸造试验机可以制备出复合良好的铜-锌铝双金属棒。

连续铸造，复合材料，双结晶器