The effect of particle size and dist ribution of rapidly quenching NdFeB magnetic powder on the magnet-ic properties of polymer-bonded NdFeB permanent magnet was studied. The results show that the particle size and the dist ribution of rapidly quenching NdFeB magnetic powder have significant effects on the magnetic properties of polymer-bonded NdFeB permanent magnet. As long as the size and the dist ribution of rapidly quenching NdFeB powder are within the right range, high magnetic properties of polymer-bonded NdFeB permanent magnet can be ob-tained. This is mainly because the rapidly quenching NdFeB magnetic powder has high hardness and is scale-shaped. The larger the size of rapidly quenching NdFeB particles is, the more difficult it is to obtain high density of bonded NdFeB magnet. However the structure will be dest royed if the size is too small. It results in the deterioration of magnetic properties. The mechanism is also discussed.

研究了快淬NdFeB永磁粉颗粒及其分布对聚合物粘结NdFeB永磁材料性能的影响。快淬Nd-FeB永磁粉颗粒大小及其分布显著地影响聚合物粘结NdFeB永磁材料的磁性能，适当尺寸的快淬Nd-FeB磁粉组合可获得高性能的粘结NdFeB永磁材料。这主要是由于快淬NdFeB磁粉硬度高，呈鳞片状，其尺寸越大越难获得高密度，但尺寸太小又将破坏磁粉的结构，导致磁性能恶化。

采用快淬、热处理及模压成形工艺，制备了成分为Nd10.5Fe78.4-xCo5ZrxB6.1（x＝0，1.0，1.5，2.0，2.5）的5种粘结永磁体。采用XRD，DTA，TEM等方法对合金的组织结构和晶化行为进行了研究。结果表明：Zr含量的增加可提高材料的非晶形成能力；当Zr添加到一定量时，形成高熔点的Fe2Zr相，产生细化晶粒的作用；添加Zr元素显著地提高了合金的矫顽力，改善了退磁曲线矩形度，从而提高了最大磁能积。Nd10.5Fe78.4-xCo5ZrxB6.1永磁体在x＝2时获得最佳磁性能，Br＝0.659T，Hcj＝628kA/m，Hcb＝419kA/m，（BH）m=73kJ/m3。

通过X射线衍射（XRD）、扫描电镜（SEM）和能谱分析（EDX）等手段重点研究了Sm-Fe17合金在氢化2歧化过程中的相组成、相的变化以及微观结构的演化规律。研究表明：在0.1MPa的H2气氛下，Sm-Fe17合金首先吸氢；400℃时合金出现部分脱氢现象；在T≥500℃逐渐开始歧化为SmHx和α2Fe，同时生成了大量的微晶或非晶组织；随着温度的升高，合金中的微晶非晶逐渐晶化，750℃时晶化完全，晶粒长大至20～100nm。通过对Sm-Fe17合金的氢化2歧化过程研究，建立了该过程的微观结构变化规律的物理模型。

研究了H2压力、温度对NdFeB铸块和铸片吸氢的影响。结果表明。NdFeB铸块和铸片在吸氢过程中均明显存在孕育期。其吸氢过程均可分为4个阶段：孕育期阶段、慢速吸氢阶段、快速吸氢阶段和缓慢吸氢阶段。随着H2压力（1×105Pa-4×105Pa）和温度（293K～373K）的升高，NdFeB铸块和铸片的吸氢速度加快，孕育期缩短。且当温度升至一定程度时，铸块的孕育期消失，而铸片的吸氢始终存在孕育期。铸片吸氢过程中的Ⅰ，Ⅱ，Ⅲ阶段的吸氢时间均明显长于铸块，而第Ⅳ阶段的吸氢时间则较短。研究同时表明。NdFeB铸块和铸片的吸氢量几乎不受氢气压力的影响，但随温度的升高，吸氢量减少。