The low-temperature magnetoresistance (LTMR) in hydrothermally synthesized La0.98Ca0.02MnO3-δ/y-Mn2O3 granular system was investigated. As-prepared powders are amorphous except for a small amount of crystalline phase LaCO3OH. After sintered at 1073K or above, La0.98Ca0.02MnO3-δ perovskite and secondary phase y-Mn2O3 coexist. A large LTMR of ~65% at 127 K and ~50% at 0 K in the sample with mean grain size of 23nm was observed. The observation of a large magnetoreslstance over a wide temperature interval could be of importance for useful applications.
powder processing, nanoparticles, ceramics, magnetotransport
-
31浏览
-
0点赞
-
0收藏
-
0分享
-
86下载
-
0
-
引用
【期刊论文】钙钛矿型锰氧化物La0.7Sr0.3Mn03的磁谱研究*
王锦辉, 朱浩, 顾本喜, 钟伟, 都有为
南京大学学报(自然科学),2002,38(2):223~227,-0001,():
-1年11月30日
报导了钙钛矿型锰氧化物La0.7Sr0.3Mn03多晶材料不同温度下磁谱的初步研究结果。平均粒径分别为45、66、105、140和1200nm的样品由溶胶一凝胶法制备。当平均粒径大于105nm时,样品的磁谱为典型的弛豫型谱线。共振频率和准静态磁导率随温度降低而减少;随平均粒径增加,准静态磁导率增大,而共振频率却减小。当平均粒径小于66nm时,观察不到类似的弛豫。实验结果显示,弛豫谱线主要是由于畴壁位移造成的,而畴壁位移的阻尼主要是与畴壁位移相联系的微观涡流效应。
磁谱,, 畴壁弛豫,, 涡流效应,, 溶胶一凝胶法
-
30浏览
-
0点赞
-
0收藏
-
0分享
-
156下载
-
0
-
引用
王锦辉, 夏樟根, 陈民溥, 赵铁松
物理与工程,2006,16(4):34~35,-0001,():
-1年11月30日
本文中初步讨论了电压敏感型惠斯登电桥的灵敏度、有效数字以及数字万用表内阻引起的误差。
惠斯登电桥, 灵敏度, 有效数字, 误差
-
58浏览
-
0点赞
-
0收藏
-
0分享
-
111下载
-
0
-
引用
王锦辉, 王昱达, 朱蕙, 黄学东, 赵铁松
物理实验,2007,27(2):35~36,-0001,():
-1年11月30日
通过固相烧结法制备了具有特大磁电阻效应的钙钛矿材料Pr0.64Ag0.044MnAl0.2O3。利用结构和成分分析,发现此材料只有在1100℃高温烧结下才能生成完整的钙钛矿结构,且属于立方晶系,晶格常量a≈0.386nm。在0.4T的外磁场下,磁电阻值在122K处达到最大,约为19.2%,为巨磁电阻实验提供了较好的样品。
钙钛矿, 微结构, 居里温度, 磁电阻效应
-
38浏览
-
0点赞
-
0收藏
-
0分享
-
129下载
-
0
-
引用
王锦辉, 黄学东, 杨文明, 夏樟根, 陈民溥, 赵铁松
物理实验,2005,25(3):31~32,-0001,():
-1年11月30日
利用RL交流电桥测量了磁性材料的居里温度,并讨论了工作频率和工作电压的变化对测量结果的影响。
居里温度, RL交流电桥, 磁性测量, 磁性材料
-