Mesophase spheres were prepared through homogeneous and heterogeneous nucleation from two coal tar pitches with some and nearly without quinoline insolubles. The pitches suffered thermal condensation in a stainless steel reactor at 440 and 410℃ for 1 or 7h, respectively. SEM was introduced as a useful tool to detect the structures of the two kinds of mesophase spheres. As a result of the paper, it was found that the structure of mesophase spheres prepared through homogeneous nucleation was Brooks-Taylor type, which is consistent with the analysis result of optical microscopy. Whereas, the structures of the heterogeneous nucleation mesophase spheres were complex, which were parallel in parts of the structure.

以石油系中间相沥青为原料，在一圆形不锈钢模具中经过460℃-30min的发泡后获得了泡沫炭生料，泡沫炭生料经过氧化、炭化和石墨化处理获得了具有良好孔结构的泡沫炭。利用SEM和偏振光显微镜观察了泡沫炭的形态和孔结构，并利用XRD方法分析了炭化和石墨化泡沫炭的微观结构。发现调整发泡时模具中的自由空间可以控制泡沫炭的孔径；炭化后中泡沫炭的孔径减小，孔壁分子取向变好，石墨化后这种作用得到了强化，使泡沫炭的结构接近石墨；泡沫炭的孔壁由平直孔壁和“Y”形孔壁结构成，前者内部分子取向优于后者，且平直孔壁两侧的分子取向优于其内部分子。大孔径的泡沫炭具有更好的内部分子取向，但其微晶尺寸较小。

炭质中间相是制备炭材料，尤其是高附加值炭材料的优质前驱体。它在高性能炭纤维、超高功率电极用针状焦、锂离子二次电池负极、超高比表面积活性炭及催化剂载体、泡沫炭等领域得到了较好的应用。本文综述了原料和热缩聚条件对炭质中间相形成和发展的影响，这些影响因素包括原料的种类、热缩聚温度、反应压力和停留时间等。通过讨论指出，由于炭质中间相涉及的原料种类多样，热缩聚制备过程中涉及的反应、物相复杂，因此，在制备特定性能的产品时，应针对产品的特定性能要求来选择原料、设定热缩聚条件，以制得具有最佳结构和性能的产品。

在制备炭质中间相的过程中，为了调整中间相形成的速度、获得特种中间相产品或研究中间相的形成机理，研究者们往往向制备中间相的原料中添加某些添加剂，这些添加剂的存在对中间相的形成过程和生成方式产生了影响。另外，在外加场（如力场、磁场、电场）的作用下，中间相分子的取向发展也会受到一定的影响。本文主要讨论添加剂（包括物理添加剂和化学添加剂）存在下中间相形成的特征以及外加场（力场、磁场和电场）对中间相形成和发展的影响，并利用“粒状基本单元构筑”中间相形成理论对这些影响因素的作用机理给予了合理的解释。